PA12 (Nylon)

3D printing material PA12-L 1600 fine polyamide powder is ideal for a wide range of prototyping and rapid manufacturing applications.

KEY BENEFITS

General purpose material with excellent mechanical properties and high elongation at break
Low water absorption and easy to process
Good recyclability

TECHNICAL SPECIFICATIONS

APPEARANCE	White
PRINTING PROCESS	Selective laser sintering
MAXIMUM PART DIMENSIONS	1000×500×450mm
LAYER THICKNESS	0.06~0.3mm adjustable
LASER TYPE	2 x CO2 100W
SCAN SPEED	15.2 m/s
MAX. CHAMBER TEMPERATURE	220°C
TENSILE STRENGTH	46MPa
TENSILE MODULUS	1602MPa
FLEXURAL STRENGTH	46.3 MPa
FLEXURAL MODULUS	1300MPa
IMPACT STRENGTH	13.2 KJ/M2
HEAT DEFLECTION TEMPERATURE (1.8 MPA)	83.5 °C